EN-MC21210 Magnesium vs. AWS BAg-2

EN-MC21210 magnesium belongs to the magnesium alloys classification, while AWS BAg-2 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21210 magnesium and the bottom bar is AWS BAg-2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 44
82
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 17
31
Tensile Strength: Ultimate (UTS), MPa 190
180

Thermal Properties

Latent Heat of Fusion, J/g 350
130
Melting Completion (Liquidus), °C 600
700
Melting Onset (Solidus), °C 570
610
Specific Heat Capacity, J/kg-K 1000
310
Thermal Expansion, µm/m-K 27
22

Otherwise Unclassified Properties

Density, g/cm3 1.6
8.9
Embodied Carbon, kg CO2/kg material 24
35
Embodied Energy, MJ/kg 160
550

Common Calculations

Stiffness to Weight: Axial, points 15
5.1
Stiffness to Weight: Bending, points 72
16
Strength to Weight: Axial, points 32
5.6
Strength to Weight: Bending, points 44
7.9
Thermal Shock Resistance, points 11
7.0

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 1.6 to 2.6
0
Cadmium (Cd), % 0
17 to 19
Copper (Cu), % 0 to 0.010
25 to 27
Iron (Fe), % 0 to 0.0050
0
Magnesium (Mg), % 96.3 to 98.3
0
Manganese (Mn), % 0.1 to 0.7
0
Nickel (Ni), % 0 to 0.0020
0
Silicon (Si), % 0 to 0.1
0
Silver (Ag), % 0
34 to 36
Zinc (Zn), % 0 to 0.2
19 to 23
Residuals, % 0 to 0.010
0 to 0.15