EN-MC21210 Magnesium vs. EN 1.4011 Stainless Steel

EN-MC21210 magnesium belongs to the magnesium alloys classification, while EN 1.4011 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21210 magnesium and the bottom bar is EN 1.4011 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 44
190
Elongation at Break, % 14
17
Fatigue Strength, MPa 70
310
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 17
76
Tensile Strength: Ultimate (UTS), MPa 190
700
Tensile Strength: Yield (Proof), MPa 90
510

Thermal Properties

Latent Heat of Fusion, J/g 350
270
Maximum Temperature: Mechanical, °C 100
750
Melting Completion (Liquidus), °C 600
1450
Melting Onset (Solidus), °C 570
1400
Specific Heat Capacity, J/kg-K 1000
480
Thermal Conductivity, W/m-K 120
25
Thermal Expansion, µm/m-K 27
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 24
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 130
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 12
7.0
Density, g/cm3 1.6
7.8
Embodied Carbon, kg CO2/kg material 24
2.0
Embodied Energy, MJ/kg 160
28
Embodied Water, L/kg 980
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 22
110
Resilience: Unit (Modulus of Resilience), kJ/m3 92
660
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 72
25
Strength to Weight: Axial, points 32
25
Strength to Weight: Bending, points 44
23
Thermal Diffusivity, mm2/s 76
6.7
Thermal Shock Resistance, points 11
24

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 1.6 to 2.6
0
Carbon (C), % 0
0 to 0.15
Chromium (Cr), % 0
11.5 to 13.5
Copper (Cu), % 0 to 0.010
0
Iron (Fe), % 0 to 0.0050
82.8 to 88.5
Magnesium (Mg), % 96.3 to 98.3
0
Manganese (Mn), % 0.1 to 0.7
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0 to 0.0020
0 to 1.0
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0 to 0.1
0 to 1.0
Sulfur (S), % 0
0 to 0.025
Zinc (Zn), % 0 to 0.2
0
Residuals, % 0 to 0.010
0