EN-MC21310 Magnesium vs. AISI 416 Stainless Steel
EN-MC21310 magnesium belongs to the magnesium alloys classification, while AISI 416 stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN-MC21310 magnesium and the bottom bar is AISI 416 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 60 | |
| 230 to 320 |
| Elastic (Young's, Tensile) Modulus, GPa | 45 | |
| 190 |
| Elongation at Break, % | 9.0 | |
| 13 to 31 |
| Fatigue Strength, MPa | 86 | |
| 230 to 340 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 17 | |
| 76 |
| Shear Strength, MPa | 120 | |
| 340 to 480 |
| Tensile Strength: Ultimate (UTS), MPa | 200 | |
| 510 to 800 |
| Tensile Strength: Yield (Proof), MPa | 120 | |
| 290 to 600 |
Thermal Properties
| Latent Heat of Fusion, J/g | 360 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 100 | |
| 680 |
| Melting Completion (Liquidus), °C | 600 | |
| 1530 |
| Melting Onset (Solidus), °C | 560 | |
| 1480 |
| Specific Heat Capacity, J/kg-K | 1000 | |
| 480 |
| Thermal Conductivity, W/m-K | 89 | |
| 30 |
| Thermal Expansion, µm/m-K | 26 | |
| 9.9 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 22 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 3.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 7.0 |
| Density, g/cm3 | 1.6 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 23 | |
| 1.9 |
| Embodied Energy, MJ/kg | 160 | |
| 27 |
| Embodied Water, L/kg | 970 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 16 | |
| 98 to 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 | |
| 220 to 940 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 73 | |
| 25 |
| Strength to Weight: Axial, points | 34 | |
| 18 to 29 |
| Strength to Weight: Bending, points | 47 | |
| 18 to 25 |
| Thermal Diffusivity, mm2/s | 55 | |
| 8.1 |
| Thermal Shock Resistance, points | 12 | |
| 19 to 30 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 1.8 to 2.6 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.15 |
| Chromium (Cr), % | 0 | |
| 12 to 14 |
| Copper (Cu), % | 0 to 0.010 | |
| 0 |
| Iron (Fe), % | 0 to 0.0050 | |
| 83.2 to 87.9 |
| Magnesium (Mg), % | 95.2 to 97.4 | |
| 0 |
| Manganese (Mn), % | 0.1 to 0.7 | |
| 0 to 1.3 |
| Nickel (Ni), % | 0 to 0.0020 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.060 |
| Silicon (Si), % | 0.7 to 1.2 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0.15 to 0.35 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 |
| Residuals, % | 0 to 0.010 | |
| 0 |