EN-MC21310 Magnesium vs. C19200 Copper

EN-MC21310 magnesium belongs to the magnesium alloys classification, while C19200 copper belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21310 magnesium and the bottom bar is C19200 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
120
Elongation at Break, % 9.0
2.0 to 35
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 17
44
Shear Strength, MPa 120
190 to 300
Tensile Strength: Ultimate (UTS), MPa 200
280 to 530
Tensile Strength: Yield (Proof), MPa 120
98 to 510

Thermal Properties

Latent Heat of Fusion, J/g 360
210
Maximum Temperature: Mechanical, °C 100
200
Melting Completion (Liquidus), °C 600
1080
Melting Onset (Solidus), °C 560
1080
Specific Heat Capacity, J/kg-K 1000
390
Thermal Conductivity, W/m-K 89
240
Thermal Expansion, µm/m-K 26
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 22
58 to 74
Electrical Conductivity: Equal Weight (Specific), % IACS 120
58 to 75

Otherwise Unclassified Properties

Base Metal Price, % relative 12
30
Density, g/cm3 1.6
8.9
Embodied Carbon, kg CO2/kg material 23
2.6
Embodied Energy, MJ/kg 160
41
Embodied Water, L/kg 970
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 16
10 to 98
Resilience: Unit (Modulus of Resilience), kJ/m3 160
42 to 1120
Stiffness to Weight: Axial, points 15
7.2
Stiffness to Weight: Bending, points 73
18
Strength to Weight: Axial, points 34
8.8 to 17
Strength to Weight: Bending, points 47
11 to 16
Thermal Diffusivity, mm2/s 55
69
Thermal Shock Resistance, points 12
10 to 19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 1.8 to 2.6
0
Copper (Cu), % 0 to 0.010
98.5 to 99.19
Iron (Fe), % 0 to 0.0050
0.8 to 1.2
Lead (Pb), % 0
0 to 0.030
Magnesium (Mg), % 95.2 to 97.4
0
Manganese (Mn), % 0.1 to 0.7
0
Nickel (Ni), % 0 to 0.0020
0
Phosphorus (P), % 0
0.010 to 0.040
Silicon (Si), % 0.7 to 1.2
0
Zinc (Zn), % 0 to 0.2
0 to 0.2
Residuals, % 0 to 0.010
0 to 0.2