EN-MC21320 Magnesium vs. EN 1.3533 Steel

EN-MC21320 magnesium belongs to the magnesium alloys classification, while EN 1.3533 steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21320 magnesium and the bottom bar is EN 1.3533 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 68
210 to 220
Elastic (Young's, Tensile) Modulus, GPa 45
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 18
73
Tensile Strength: Ultimate (UTS), MPa 230
690 to 1420

Thermal Properties

Latent Heat of Fusion, J/g 370
250
Maximum Temperature: Mechanical, °C 110
440
Melting Completion (Liquidus), °C 600
1460
Melting Onset (Solidus), °C 530
1420
Specific Heat Capacity, J/kg-K 1000
470
Thermal Conductivity, W/m-K 66
47
Thermal Expansion, µm/m-K 26
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 17
7.9
Electrical Conductivity: Equal Weight (Specific), % IACS 91
9.0

Otherwise Unclassified Properties

Base Metal Price, % relative 12
5.0
Density, g/cm3 1.6
7.9
Embodied Carbon, kg CO2/kg material 23
1.8
Embodied Energy, MJ/kg 160
25
Embodied Water, L/kg 980
60

Common Calculations

Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 72
24
Strength to Weight: Axial, points 38
24 to 50
Strength to Weight: Bending, points 50
22 to 36
Thermal Diffusivity, mm2/s 40
13
Thermal Shock Resistance, points 13
20 to 42

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 3.5 to 5.0
0 to 0.050
Carbon (C), % 0
0.15 to 0.2
Chromium (Cr), % 0
1.3 to 1.6
Copper (Cu), % 0 to 0.010
0 to 0.3
Iron (Fe), % 0 to 0.0050
92.9 to 94.9
Magnesium (Mg), % 92.5 to 95.9
0
Manganese (Mn), % 0.1 to 0.7
0.4 to 0.7
Molybdenum (Mo), % 0
0.15 to 0.25
Nickel (Ni), % 0 to 0.0020
3.3 to 3.8
Oxygen (O), % 0
0 to 0.0020
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0.5 to 1.5
0 to 0.4
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 0 to 0.2
0
Residuals, % 0 to 0.010
0