MakeItFrom.com
Menu (ESC)

EN-MC65210 Magnesium vs. EN 1.4832 Stainless Steel

EN-MC65210 magnesium belongs to the magnesium alloys classification, while EN 1.4832 stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC65210 magnesium and the bottom bar is EN 1.4832 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 80
150
Elastic (Young's, Tensile) Modulus, GPa 44
200
Elongation at Break, % 2.8
11
Fatigue Strength, MPa 110
140
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 17
77
Tensile Strength: Ultimate (UTS), MPa 270
510
Tensile Strength: Yield (Proof), MPa 200
260

Thermal Properties

Latent Heat of Fusion, J/g 340
310
Maximum Temperature: Mechanical, °C 170
950
Melting Completion (Liquidus), °C 610
1400
Melting Onset (Solidus), °C 540
1360
Specific Heat Capacity, J/kg-K 970
480
Thermal Conductivity, W/m-K 110
14
Thermal Expansion, µm/m-K 26
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 25
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 110
2.5

Otherwise Unclassified Properties

Density, g/cm3 2.0
7.8
Embodied Carbon, kg CO2/kg material 27
3.6
Embodied Energy, MJ/kg 220
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.9
48
Resilience: Unit (Modulus of Resilience), kJ/m3 450
170
Stiffness to Weight: Axial, points 12
14
Stiffness to Weight: Bending, points 59
25
Strength to Weight: Axial, points 38
18
Strength to Weight: Bending, points 47
18
Thermal Diffusivity, mm2/s 58
3.7
Thermal Shock Resistance, points 17
12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.15 to 0.35
Chromium (Cr), % 0
19 to 21
Copper (Cu), % 0 to 0.030
0
Iron (Fe), % 0 to 0.010
58.6 to 67.4
Magnesium (Mg), % 92.6 to 95.6
0
Manganese (Mn), % 0 to 0.15
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0 to 0.0050
13 to 15
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.010
0.5 to 2.5
Silver (Ag), % 2.0 to 3.0
0
Sulfur (S), % 0
0 to 0.030
Unspecified Rare Earths, % 2.0 to 3.0
0
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010
0