EN-MC95310 Magnesium vs. AISI 310H Stainless Steel

EN-MC95310 magnesium belongs to the magnesium alloys classification, while AISI 310H stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC95310 magnesium and the bottom bar is AISI 310H stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 85
190
Elastic (Young's, Tensile) Modulus, GPa 45
200
Elongation at Break, % 2.2
40
Fatigue Strength, MPa 110
200
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 17
79
Shear Strength, MPa 160
400
Tensile Strength: Ultimate (UTS), MPa 280
580
Tensile Strength: Yield (Proof), MPa 190
230

Thermal Properties

Latent Heat of Fusion, J/g 330
300
Maximum Temperature: Mechanical, °C 170
1100
Melting Completion (Liquidus), °C 650
1410
Melting Onset (Solidus), °C 540
1360
Specific Heat Capacity, J/kg-K 960
480
Thermal Conductivity, W/m-K 51
15
Thermal Expansion, µm/m-K 25
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 50
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 34
25
Density, g/cm3 1.9
7.9
Embodied Carbon, kg CO2/kg material 29
4.3
Embodied Energy, MJ/kg 260
61
Embodied Water, L/kg 900
190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 5.6
190
Resilience: Unit (Modulus of Resilience), kJ/m3 420
130
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 61
25
Strength to Weight: Axial, points 40
21
Strength to Weight: Bending, points 49
20
Thermal Diffusivity, mm2/s 28
3.9
Thermal Shock Resistance, points 18
13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.040 to 0.1
Chromium (Cr), % 0
24 to 26
Copper (Cu), % 0 to 0.030
0
Iron (Fe), % 0 to 0.010
49.1 to 57
Lithium (Li), % 0 to 0.2
0
Magnesium (Mg), % 88.9 to 93.4
0
Manganese (Mn), % 0 to 0.15
0 to 2.0
Nickel (Ni), % 0 to 0.0050
19 to 22
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0 to 0.010
0 to 0.75
Sulfur (S), % 0
0 to 0.030
Unspecified Rare Earths, % 1.5 to 4.0
0
Yttrium (Y), % 4.8 to 5.5
0
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.010
0