H06 C52400 Bronze vs. H06 C53400 Bronze
Both H06 C52400 bronze and H06 C53400 bronze are copper alloys. Both are furnished in the H06 (extra hard) temper. They have a moderately high 95% of their average alloy composition in common.
For each property being compared, the top bar is H06 C52400 bronze and the bottom bar is H06 C53400 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Rockwell B Hardness | 100 | |
| 90 |
| Rockwell Superficial 30T Hardness | 82 | |
| 77 |
| Shear Modulus, GPa | 41 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 790 | |
| 630 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 180 |
| Melting Completion (Liquidus), °C | 1000 | |
| 1050 |
| Melting Onset (Solidus), °C | 840 | |
| 950 |
| Specific Heat Capacity, J/kg-K | 370 | |
| 380 |
| Thermal Conductivity, W/m-K | 50 | |
| 69 |
| Thermal Expansion, µm/m-K | 18 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 15 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 11 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 35 | |
| 32 |
| Density, g/cm3 | 8.8 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 3.0 |
| Embodied Energy, MJ/kg | 58 | |
| 49 |
| Embodied Water, L/kg | 390 | |
| 350 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.9 | |
| 7.0 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 25 | |
| 20 |
| Strength to Weight: Bending, points | 22 | |
| 18 |
| Thermal Diffusivity, mm2/s | 15 | |
| 21 |
| Thermal Shock Resistance, points | 29 | |
| 23 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 87.8 to 91 | |
| 91.8 to 95.7 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.050 | |
| 0.8 to 1.2 |
| Phosphorus (P), % | 0.030 to 0.35 | |
| 0.030 to 0.35 |
| Tin (Sn), % | 9.0 to 11 | |
| 3.5 to 5.8 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 to 0.3 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |