Grade 1 Babbitt Metal vs. Solder Alloy 811
Both grade 1 Babbitt Metal and solder alloy 811 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 89% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is grade 1 Babbitt Metal and the bottom bar is solder alloy 811.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 53 | |
| 52 |
| Elongation at Break, % | 34 | |
| 38 |
| Poisson's Ratio | 0.35 | |
| 0.35 |
| Shear Modulus, GPa | 20 | |
| 19 |
Thermal Properties
| Latent Heat of Fusion, J/g | 70 | |
| 63 |
| Melting Completion (Liquidus), °C | 370 | |
| 200 |
| Melting Onset (Solidus), °C | 220 | |
| 190 |
| Specific Heat Capacity, J/kg-K | 230 | |
| 230 |
| Thermal Conductivity, W/m-K | 45 | |
| 59 |
| Thermal Expansion, µm/m-K | 21 | |
| 22 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 13 | |
| 14 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 16 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.3 | |
| 7.3 |
| Embodied Carbon, kg CO2/kg material | 12 | |
| 14 |
| Embodied Energy, MJ/kg | 200 | |
| 240 |
| Embodied Water, L/kg | 1160 | |
| 1200 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.0 | |
| 4.0 |
| Stiffness to Weight: Bending, points | 17 | |
| 17 |
| Thermal Diffusivity, mm2/s | 26 | |
| 35 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 4.0 to 5.0 | |
| 0 to 0.1 |
| Arsenic (As), % | 0 to 0.1 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 to 0.080 | |
| 2.8 to 3.2 |
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 to 0.0020 |
| Copper (Cu), % | 4.0 to 5.0 | |
| 0 to 0.050 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.080 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 to 0.35 | |
| 0 to 0.070 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Silver (Ag), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 89.3 to 92 | |
| 87.8 to 89.7 |
| Zinc (Zn), % | 0 to 0.0050 | |
| 7.5 to 8.5 |