Grade 21 Titanium vs. EN 1.5537 Steel
Grade 21 titanium belongs to the titanium alloys classification, while EN 1.5537 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is grade 21 titanium and the bottom bar is EN 1.5537 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 190 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Reduction in Area, % | 22 | |
| 64 to 69 |
| Shear Modulus, GPa | 51 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 890 to 1340 | |
| 520 to 1760 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 310 | |
| 400 |
| Melting Completion (Liquidus), °C | 1740 | |
| 1460 |
| Melting Onset (Solidus), °C | 1690 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 470 |
| Thermal Conductivity, W/m-K | 7.5 | |
| 48 |
| Thermal Expansion, µm/m-K | 7.1 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 1.9 |
| Density, g/cm3 | 5.4 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 32 | |
| 1.4 |
| Embodied Energy, MJ/kg | 490 | |
| 19 |
| Embodied Water, L/kg | 180 | |
| 47 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 32 | |
| 24 |
| Strength to Weight: Axial, points | 46 to 69 | |
| 18 to 63 |
| Strength to Weight: Bending, points | 38 to 50 | |
| 18 to 41 |
| Thermal Diffusivity, mm2/s | 2.8 | |
| 13 |
| Thermal Shock Resistance, points | 66 to 100 | |
| 15 to 52 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 2.5 to 3.5 | |
| 0 |
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0 to 0.050 | |
| 0.33 to 0.38 |
| Chromium (Cr), % | 0 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.4 | |
| 97.6 to 98.9 |
| Manganese (Mn), % | 0 | |
| 0.8 to 1.1 |
| Molybdenum (Mo), % | 14 to 16 | |
| 0 |
| Niobium (Nb), % | 2.2 to 3.2 | |
| 0 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.17 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0.15 to 0.25 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 | |
| 0 to 0.025 |
| Titanium (Ti), % | 76 to 81.2 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |