Grade 21 Titanium vs. Grade 250 Maraging Steel
Grade 21 titanium belongs to the titanium alloys classification, while grade 250 maraging steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is grade 21 titanium and the bottom bar is grade 250 maraging steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 190 |
| Elongation at Break, % | 9.0 to 17 | |
| 7.3 to 17 |
| Poisson's Ratio | 0.32 | |
| 0.3 |
| Shear Modulus, GPa | 51 | |
| 75 |
| Shear Strength, MPa | 550 to 790 | |
| 600 to 1060 |
| Tensile Strength: Ultimate (UTS), MPa | 890 to 1340 | |
| 970 to 1800 |
| Tensile Strength: Yield (Proof), MPa | 870 to 1170 | |
| 660 to 1740 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 270 |
| Melting Completion (Liquidus), °C | 1740 | |
| 1480 |
| Melting Onset (Solidus), °C | 1690 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 450 |
| Thermal Expansion, µm/m-K | 7.1 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 32 |
| Density, g/cm3 | 5.4 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 32 | |
| 4.9 |
| Embodied Energy, MJ/kg | 490 | |
| 65 |
| Embodied Water, L/kg | 180 | |
| 140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 180 | |
| 130 to 150 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 32 | |
| 23 |
| Strength to Weight: Axial, points | 46 to 69 | |
| 33 to 61 |
| Strength to Weight: Bending, points | 38 to 50 | |
| 26 to 40 |
| Thermal Shock Resistance, points | 66 to 100 | |
| 29 to 54 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 2.5 to 3.5 | |
| 0.050 to 0.15 |
| Boron (B), % | 0 | |
| 0 to 0.0030 |
| Calcium (Ca), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0 to 0.050 | |
| 0 to 0.030 |
| Cobalt (Co), % | 0 | |
| 7.0 to 8.5 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.4 | |
| 66.3 to 71.1 |
| Manganese (Mn), % | 0 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 14 to 16 | |
| 4.6 to 5.2 |
| Nickel (Ni), % | 0 | |
| 17 to 19 |
| Niobium (Nb), % | 2.2 to 3.2 | |
| 0 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.17 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.010 |
| Silicon (Si), % | 0.15 to 0.25 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Titanium (Ti), % | 76 to 81.2 | |
| 0.3 to 0.5 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.020 |
| Residuals, % | 0 to 0.4 | |
| 0 |