Grade 21 Titanium vs. C72200 Copper-nickel
Grade 21 titanium belongs to the titanium alloys classification, while C72200 copper-nickel belongs to the copper alloys. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is grade 21 titanium and the bottom bar is C72200 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 130 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 51 | |
| 48 |
| Tensile Strength: Ultimate (UTS), MPa | 890 to 1340 | |
| 350 to 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 220 |
| Maximum Temperature: Mechanical, °C | 310 | |
| 230 |
| Melting Completion (Liquidus), °C | 1740 | |
| 1180 |
| Melting Onset (Solidus), °C | 1690 | |
| 1120 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 400 |
| Thermal Conductivity, W/m-K | 7.5 | |
| 34 |
| Thermal Expansion, µm/m-K | 7.1 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 36 |
| Density, g/cm3 | 5.4 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 32 | |
| 3.9 |
| Embodied Energy, MJ/kg | 490 | |
| 59 |
| Embodied Water, L/kg | 180 | |
| 300 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 8.0 |
| Stiffness to Weight: Bending, points | 32 | |
| 19 |
| Strength to Weight: Axial, points | 46 to 69 | |
| 11 to 18 |
| Strength to Weight: Bending, points | 38 to 50 | |
| 12 to 17 |
| Thermal Diffusivity, mm2/s | 2.8 | |
| 9.6 |
| Thermal Shock Resistance, points | 66 to 100 | |
| 12 to 20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 2.5 to 3.5 | |
| 0 |
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0.3 to 0.7 |
| Copper (Cu), % | 0 | |
| 78.1 to 84.2 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.4 | |
| 0.5 to 1.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 14 to 16 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 15 to 18 |
| Niobium (Nb), % | 2.2 to 3.2 | |
| 0 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.17 | |
| 0 |
| Silicon (Si), % | 0.15 to 0.25 | |
| 0 |
| Titanium (Ti), % | 76 to 81.2 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 1.0 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.2 |