Grade 21 Titanium vs. N08800 Stainless Steel
Grade 21 titanium belongs to the titanium alloys classification, while N08800 stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is grade 21 titanium and the bottom bar is N08800 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 200 |
| Elongation at Break, % | 9.0 to 17 | |
| 4.5 to 34 |
| Fatigue Strength, MPa | 550 to 660 | |
| 150 to 390 |
| Poisson's Ratio | 0.32 | |
| 0.28 |
| Shear Modulus, GPa | 51 | |
| 77 |
| Shear Strength, MPa | 550 to 790 | |
| 340 to 580 |
| Tensile Strength: Ultimate (UTS), MPa | 890 to 1340 | |
| 500 to 1000 |
| Tensile Strength: Yield (Proof), MPa | 870 to 1170 | |
| 190 to 830 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 300 |
| Maximum Temperature: Mechanical, °C | 310 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1740 | |
| 1390 |
| Melting Onset (Solidus), °C | 1690 | |
| 1360 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 480 |
| Thermal Conductivity, W/m-K | 7.5 | |
| 12 |
| Thermal Expansion, µm/m-K | 7.1 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 30 |
| Density, g/cm3 | 5.4 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 32 | |
| 5.3 |
| Embodied Energy, MJ/kg | 490 | |
| 76 |
| Embodied Water, L/kg | 180 | |
| 200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 180 | |
| 42 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2760 to 5010 | |
| 96 to 1740 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 32 | |
| 24 |
| Strength to Weight: Axial, points | 46 to 69 | |
| 18 to 35 |
| Strength to Weight: Bending, points | 38 to 50 | |
| 18 to 28 |
| Thermal Diffusivity, mm2/s | 2.8 | |
| 3.0 |
| Thermal Shock Resistance, points | 66 to 100 | |
| 13 to 25 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 2.5 to 3.5 | |
| 0.15 to 0.6 |
| Carbon (C), % | 0 to 0.050 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0 | |
| 19 to 23 |
| Copper (Cu), % | 0 | |
| 0 to 0.75 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.4 | |
| 39.5 to 50.7 |
| Manganese (Mn), % | 0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 14 to 16 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 30 to 35 |
| Niobium (Nb), % | 2.2 to 3.2 | |
| 0 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.17 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.045 |
| Silicon (Si), % | 0.15 to 0.25 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Titanium (Ti), % | 76 to 81.2 | |
| 0.15 to 0.6 |
| Residuals, % | 0 to 0.4 | |
| 0 |