Grade 21 Titanium vs. R60901 Alloy
Grade 21 titanium belongs to the titanium alloys classification, while R60901 alloy belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is grade 21 titanium and the bottom bar is R60901 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 98 |
| Elongation at Break, % | 9.0 to 17 | |
| 17 to 22 |
| Poisson's Ratio | 0.32 | |
| 0.34 |
| Shear Modulus, GPa | 51 | |
| 37 |
| Tensile Strength: Ultimate (UTS), MPa | 890 to 1340 | |
| 500 to 580 |
| Tensile Strength: Yield (Proof), MPa | 870 to 1170 | |
| 350 to 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 270 |
| Thermal Conductivity, W/m-K | 7.5 | |
| 17 |
| Thermal Expansion, µm/m-K | 7.1 | |
| 6.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 5.4 | |
| 6.6 |
| Embodied Water, L/kg | 180 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 180 | |
| 88 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2760 to 5010 | |
| 640 to 760 |
| Stiffness to Weight: Axial, points | 14 | |
| 8.3 |
| Stiffness to Weight: Bending, points | 32 | |
| 23 |
| Strength to Weight: Axial, points | 46 to 69 | |
| 21 to 25 |
| Strength to Weight: Bending, points | 38 to 50 | |
| 21 to 24 |
| Thermal Diffusivity, mm2/s | 2.8 | |
| 9.7 |
| Thermal Shock Resistance, points | 66 to 100 | |
| 58 to 67 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 2.5 to 3.5 | |
| 0 |
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 |
| Molybdenum (Mo), % | 14 to 16 | |
| 0 |
| Niobium (Nb), % | 2.2 to 3.2 | |
| 2.4 to 2.8 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.17 | |
| 0 |
| Silicon (Si), % | 0.15 to 0.25 | |
| 0 |
| Titanium (Ti), % | 76 to 81.2 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 96.8 to 97.5 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.29 |