Grade 24 Titanium vs. 6018 Aluminum
Grade 24 titanium belongs to the titanium alloys classification, while 6018 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is grade 24 titanium and the bottom bar is 6018 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 69 |
| Elongation at Break, % | 11 | |
| 9.0 to 9.1 |
| Fatigue Strength, MPa | 550 | |
| 85 to 89 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 40 | |
| 26 |
| Shear Strength, MPa | 610 | |
| 170 to 180 |
| Tensile Strength: Ultimate (UTS), MPa | 1010 | |
| 290 to 300 |
| Tensile Strength: Yield (Proof), MPa | 940 | |
| 220 to 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 340 | |
| 160 |
| Melting Completion (Liquidus), °C | 1610 | |
| 640 |
| Melting Onset (Solidus), °C | 1560 | |
| 570 |
| Specific Heat Capacity, J/kg-K | 560 | |
| 890 |
| Thermal Conductivity, W/m-K | 7.1 | |
| 170 |
| Thermal Expansion, µm/m-K | 9.6 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.0 | |
| 44 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.0 | |
| 140 |
Otherwise Unclassified Properties
| Density, g/cm3 | 4.5 | |
| 2.9 |
| Embodied Carbon, kg CO2/kg material | 43 | |
| 8.2 |
| Embodied Energy, MJ/kg | 710 | |
| 150 |
| Embodied Water, L/kg | 310 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 24 to 25 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 4160 | |
| 360 to 380 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 35 | |
| 48 |
| Strength to Weight: Axial, points | 63 | |
| 28 to 29 |
| Strength to Weight: Bending, points | 50 | |
| 34 to 35 |
| Thermal Diffusivity, mm2/s | 2.9 | |
| 65 |
| Thermal Shock Resistance, points | 72 | |
| 13 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 5.5 to 6.8 | |
| 93.1 to 97.8 |
| Bismuth (Bi), % | 0 | |
| 0.4 to 0.7 |
| Carbon (C), % | 0 to 0.080 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 | |
| 0.15 to 0.4 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 0.7 |
| Lead (Pb), % | 0 | |
| 0.4 to 1.2 |
| Magnesium (Mg), % | 0 | |
| 0.6 to 1.2 |
| Manganese (Mn), % | 0 | |
| 0.3 to 0.8 |
| Nitrogen (N), % | 0 to 0.050 | |
| 0 |
| Oxygen (O), % | 0 to 0.2 | |
| 0 |
| Palladium (Pd), % | 0.040 to 0.080 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0.5 to 1.2 |
| Titanium (Ti), % | 87.5 to 91 | |
| 0 to 0.2 |
| Vanadium (V), % | 3.5 to 4.5 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.3 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.15 |