Grade 24 Titanium vs. AWS ERNiCrCoMo-1

Grade 24 titanium belongs to the titanium alloys classification, while AWS ERNiCrCoMo-1 belongs to the nickel alloys. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is grade 24 titanium and the bottom bar is AWS ERNiCrCoMo-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
210
Elongation at Break, % 11
28
Poisson's Ratio 0.32
0.29
Shear Modulus, GPa 40
81
Tensile Strength: Ultimate (UTS), MPa 1010
710

Thermal Properties

Latent Heat of Fusion, J/g 410
330
Melting Completion (Liquidus), °C 1610
1420
Melting Onset (Solidus), °C 1560
1370
Specific Heat Capacity, J/kg-K 560
450
Thermal Conductivity, W/m-K 7.1
13
Thermal Expansion, µm/m-K 9.6
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.0
1.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
1.5

Otherwise Unclassified Properties

Density, g/cm3 4.5
8.5
Embodied Carbon, kg CO2/kg material 43
10
Embodied Energy, MJ/kg 710
140
Embodied Water, L/kg 310
350

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 35
23
Strength to Weight: Axial, points 63
23
Strength to Weight: Bending, points 50
21
Thermal Diffusivity, mm2/s 2.9
3.5
Thermal Shock Resistance, points 72
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.5 to 6.8
0.8 to 1.5
Carbon (C), % 0 to 0.080
0.050 to 0.15
Chromium (Cr), % 0
20 to 24
Cobalt (Co), % 0
10 to 15
Copper (Cu), % 0
0 to 0.5
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.4
0 to 3.0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
8.0 to 10
Nickel (Ni), % 0
42.7 to 61.2
Nitrogen (N), % 0 to 0.050
0
Oxygen (O), % 0 to 0.2
0
Palladium (Pd), % 0.040 to 0.080
0
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.015
Titanium (Ti), % 87.5 to 91
0 to 0.6
Vanadium (V), % 3.5 to 4.5
0
Residuals, % 0 to 0.4
0 to 0.5