MakeItFrom.com
Menu (ESC)

Grade 24 Titanium vs. EN 1.4713 Stainless Steel

Grade 24 titanium belongs to the titanium alloys classification, while EN 1.4713 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is grade 24 titanium and the bottom bar is EN 1.4713 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
190
Elongation at Break, % 11
20
Fatigue Strength, MPa 550
160
Poisson's Ratio 0.32
0.29
Shear Modulus, GPa 40
74
Shear Strength, MPa 610
320
Tensile Strength: Ultimate (UTS), MPa 1010
520
Tensile Strength: Yield (Proof), MPa 940
250

Thermal Properties

Latent Heat of Fusion, J/g 410
270
Maximum Temperature: Mechanical, °C 340
800
Melting Completion (Liquidus), °C 1610
1440
Melting Onset (Solidus), °C 1560
1400
Specific Heat Capacity, J/kg-K 560
480
Thermal Conductivity, W/m-K 7.1
23
Thermal Expansion, µm/m-K 9.6
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.0
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
2.9

Otherwise Unclassified Properties

Density, g/cm3 4.5
7.7
Embodied Carbon, kg CO2/kg material 43
1.7
Embodied Energy, MJ/kg 710
24
Embodied Water, L/kg 310
84

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
84
Resilience: Unit (Modulus of Resilience), kJ/m3 4160
160
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 35
25
Strength to Weight: Axial, points 63
19
Strength to Weight: Bending, points 50
19
Thermal Diffusivity, mm2/s 2.9
6.2
Thermal Shock Resistance, points 72
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.5 to 6.8
0.5 to 1.0
Carbon (C), % 0 to 0.080
0 to 0.12
Chromium (Cr), % 0
6.0 to 8.0
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.4
88.8 to 93
Manganese (Mn), % 0
0 to 1.0
Nitrogen (N), % 0 to 0.050
0
Oxygen (O), % 0 to 0.2
0
Palladium (Pd), % 0.040 to 0.080
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0.5 to 1.0
Sulfur (S), % 0
0 to 0.015
Titanium (Ti), % 87.5 to 91
0
Vanadium (V), % 3.5 to 4.5
0
Residuals, % 0 to 0.4
0