Grade 24 Titanium vs. CR019A Copper

Grade 24 titanium belongs to the titanium alloys classification, while CR019A copper belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is grade 24 titanium and the bottom bar is CR019A copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
120
Elongation at Break, % 11
15
Poisson's Ratio 0.32
0.34
Shear Modulus, GPa 40
43
Tensile Strength: Ultimate (UTS), MPa 1010
220
Tensile Strength: Yield (Proof), MPa 940
130

Thermal Properties

Latent Heat of Fusion, J/g 410
210
Maximum Temperature: Mechanical, °C 340
200
Melting Completion (Liquidus), °C 1610
1090
Melting Onset (Solidus), °C 1560
1040
Specific Heat Capacity, J/kg-K 560
390
Thermal Conductivity, W/m-K 7.1
390
Thermal Expansion, µm/m-K 9.6
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.0
100
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
100

Otherwise Unclassified Properties

Density, g/cm3 4.5
9.0
Embodied Carbon, kg CO2/kg material 43
2.7
Embodied Energy, MJ/kg 710
42
Embodied Water, L/kg 310
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
29
Resilience: Unit (Modulus of Resilience), kJ/m3 4160
76
Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 35
18
Strength to Weight: Axial, points 63
6.8
Strength to Weight: Bending, points 50
9.0
Thermal Diffusivity, mm2/s 2.9
110
Thermal Shock Resistance, points 72
7.8

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.5 to 6.8
0
Bismuth (Bi), % 0
0 to 0.00050
Carbon (C), % 0 to 0.080
0
Copper (Cu), % 0
99.874 to 99.92
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.4
0
Nitrogen (N), % 0 to 0.050
0
Oxygen (O), % 0 to 0.2
0
Palladium (Pd), % 0.040 to 0.080
0
Silver (Ag), % 0
0.080 to 0.12
Titanium (Ti), % 87.5 to 91
0
Vanadium (V), % 3.5 to 4.5
0
Residuals, % 0 to 0.4
0