Grade 24 Titanium vs. C83600 Ounce Metal

Grade 24 titanium belongs to the titanium alloys classification, while C83600 ounce metal belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is grade 24 titanium and the bottom bar is C83600 ounce metal.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
110
Elongation at Break, % 11
21
Poisson's Ratio 0.32
0.34
Shear Modulus, GPa 40
39
Tensile Strength: Ultimate (UTS), MPa 1010
250
Tensile Strength: Yield (Proof), MPa 940
120

Thermal Properties

Latent Heat of Fusion, J/g 410
190
Maximum Temperature: Mechanical, °C 340
160
Melting Completion (Liquidus), °C 1610
1010
Melting Onset (Solidus), °C 1560
850
Specific Heat Capacity, J/kg-K 560
370
Thermal Conductivity, W/m-K 7.1
72
Thermal Expansion, µm/m-K 9.6
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.0
15
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
15

Otherwise Unclassified Properties

Density, g/cm3 4.5
8.8
Embodied Carbon, kg CO2/kg material 43
3.1
Embodied Energy, MJ/kg 710
50
Embodied Water, L/kg 310
350

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
43
Resilience: Unit (Modulus of Resilience), kJ/m3 4160
70
Stiffness to Weight: Axial, points 13
6.7
Stiffness to Weight: Bending, points 35
18
Strength to Weight: Axial, points 63
7.9
Strength to Weight: Bending, points 50
10
Thermal Diffusivity, mm2/s 2.9
22
Thermal Shock Resistance, points 72
9.3

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.5 to 6.8
0 to 0.0050
Antimony (Sb), % 0
0 to 0.25
Carbon (C), % 0 to 0.080
0
Copper (Cu), % 0
84 to 86
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.4
0 to 0.3
Lead (Pb), % 0
4.0 to 6.0
Nickel (Ni), % 0
0 to 1.0
Nitrogen (N), % 0 to 0.050
0
Oxygen (O), % 0 to 0.2
0
Palladium (Pd), % 0.040 to 0.080
0
Phosphorus (P), % 0
0 to 1.5
Silicon (Si), % 0
0 to 0.0050
Sulfur (S), % 0
0 to 0.080
Tin (Sn), % 0
4.0 to 6.0
Titanium (Ti), % 87.5 to 91
0
Vanadium (V), % 3.5 to 4.5
0
Zinc (Zn), % 0
4.0 to 6.0
Residuals, % 0 to 0.4
0 to 0.7