Grade 35 Titanium vs. Grade 37 Titanium
Both grade 35 titanium and grade 37 titanium are titanium alloys. Both are furnished in the annealed condition. They have a moderately high 93% of their average alloy composition in common.
For each property being compared, the top bar is grade 35 titanium and the bottom bar is grade 37 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 5.6 | |
| 22 |
| Fatigue Strength, MPa | 330 | |
| 170 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Reduction in Area, % | 23 | |
| 34 |
| Shear Modulus, GPa | 41 | |
| 40 |
| Shear Strength, MPa | 580 | |
| 240 |
| Tensile Strength: Ultimate (UTS), MPa | 1000 | |
| 390 |
| Tensile Strength: Yield (Proof), MPa | 630 | |
| 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 420 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 320 | |
| 310 |
| Melting Completion (Liquidus), °C | 1630 | |
| 1650 |
| Melting Onset (Solidus), °C | 1580 | |
| 1600 |
| Specific Heat Capacity, J/kg-K | 550 | |
| 550 |
| Thermal Conductivity, W/m-K | 7.4 | |
| 21 |
| Thermal Expansion, µm/m-K | 9.3 | |
| 8.9 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.1 | |
| 3.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.2 | |
| 6.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 37 | |
| 36 |
| Density, g/cm3 | 4.6 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 33 | |
| 31 |
| Embodied Energy, MJ/kg | 530 | |
| 500 |
| Embodied Water, L/kg | 170 | |
| 120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 49 | |
| 76 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1830 | |
| 280 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 35 | |
| 35 |
| Strength to Weight: Axial, points | 61 | |
| 24 |
| Strength to Weight: Bending, points | 49 | |
| 26 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 8.4 |
| Thermal Shock Resistance, points | 70 | |
| 29 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 4.0 to 5.0 | |
| 1.0 to 2.0 |
| Carbon (C), % | 0 to 0.080 | |
| 0 to 0.080 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 to 0.015 |
| Iron (Fe), % | 0.2 to 0.8 | |
| 0 to 0.3 |
| Molybdenum (Mo), % | 1.5 to 2.5 | |
| 0 |
| Nitrogen (N), % | 0 to 0.050 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 to 0.25 | |
| 0 to 0.25 |
| Silicon (Si), % | 0.2 to 0.4 | |
| 0 |
| Titanium (Ti), % | 88.4 to 93 | |
| 96.9 to 99 |
| Vanadium (V), % | 1.1 to 2.1 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.4 |