Grade 702C Zirconium vs. ASTM A182 Grade F36

Grade 702C zirconium belongs to the otherwise unclassified metals classification, while ASTM A182 grade F36 belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is ASTM A182 grade F36.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
220
Elastic (Young's, Tensile) Modulus, GPa 97
190
Elongation at Break, % 13
17
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 36
73
Tensile Strength: Ultimate (UTS), MPa 430
710
Tensile Strength: Yield (Proof), MPa 310
490

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Specific Heat Capacity, J/kg-K 270
470
Thermal Conductivity, W/m-K 22
39
Thermal Expansion, µm/m-K 5.7
13

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.9
Embodied Water, L/kg 450
53

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 52
110
Resilience: Unit (Modulus of Resilience), kJ/m3 510
650
Stiffness to Weight: Axial, points 8.1
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 18
25
Strength to Weight: Bending, points 19
22
Thermal Diffusivity, mm2/s 12
10
Thermal Shock Resistance, points 55
21

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.1
0.1 to 0.17
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 0
0.5 to 0.8
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
95 to 97.1
Manganese (Mn), % 0
0.8 to 1.2
Molybdenum (Mo), % 0
0.25 to 0.5
Nickel (Ni), % 0
1.0 to 1.3
Niobium (Nb), % 0
0.015 to 0.045
Nitrogen (N), % 0 to 0.030
0 to 0.020
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0 to 0.030
Silicon (Si), % 0
0.25 to 0.5
Sulfur (S), % 0
0 to 0.025
Vanadium (V), % 0
0 to 0.020
Zirconium (Zr), % 94.8 to 100
0