Grade 702C zirconium belongs to the otherwise unclassified metals classification, while AWS E312 belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is AWS E312.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 97
200
Elongation at Break, % 13
25
Poisson's Ratio 0.34
0.27
Shear Modulus, GPa 36
80
Tensile Strength: Ultimate (UTS), MPa 430
740

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Specific Heat Capacity, J/kg-K 270
480
Thermal Expansion, µm/m-K 5.7
15

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.7
Embodied Water, L/kg 450
200

Common Calculations

Stiffness to Weight: Axial, points 8.1
15
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 18
27
Strength to Weight: Bending, points 19
24
Thermal Shock Resistance, points 55
18

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.15
Chromium (Cr), % 0
28 to 32
Copper (Cu), % 0
0 to 0.75
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
52.3 to 63.5
Manganese (Mn), % 0
0.5 to 2.5
Molybdenum (Mo), % 0
0 to 0.75
Nickel (Ni), % 0
8.0 to 10.5
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Zirconium (Zr), % 94.8 to 100
0