Grade 704C Zirconium vs. SAE-AISI 1005 Steel

Grade 704C zirconium belongs to the otherwise unclassified metals classification, while SAE-AISI 1005 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is grade 704C zirconium and the bottom bar is SAE-AISI 1005 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
95
Elastic (Young's, Tensile) Modulus, GPa 97
190
Elongation at Break, % 11
23
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 36
73
Tensile Strength: Ultimate (UTS), MPa 470
330
Tensile Strength: Yield (Proof), MPa 310
260

Thermal Properties

Latent Heat of Fusion, J/g 240
250
Specific Heat Capacity, J/kg-K 270
470
Thermal Conductivity, W/m-K 21
53
Thermal Expansion, µm/m-K 5.9
12

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.9
Embodied Water, L/kg 460
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 48
70
Resilience: Unit (Modulus of Resilience), kJ/m3 490
180
Stiffness to Weight: Axial, points 8.1
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 20
12
Strength to Weight: Bending, points 20
13
Thermal Diffusivity, mm2/s 12
14
Thermal Shock Resistance, points 58
10

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.060
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
99.5 to 100
Manganese (Mn), % 0
0 to 0.35
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.010
0 to 0.040
Sulfur (S), % 0
0 to 0.050
Tin (Sn), % 1.0 to 2.0
0
Zirconium (Zr), % 92.9 to 99
0