Grade 9 Titanium vs. Grade 1 Titanium
Both grade 9 titanium and grade 1 titanium are titanium alloys. They have a moderately high 94% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is grade 9 titanium and the bottom bar is grade 1 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 11 to 17 | |
| 28 |
| Fatigue Strength, MPa | 330 to 480 | |
| 170 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Reduction in Area, % | 28 | |
| 36 |
| Shear Modulus, GPa | 40 | |
| 39 |
| Shear Strength, MPa | 430 to 580 | |
| 200 |
| Tensile Strength: Ultimate (UTS), MPa | 700 to 960 | |
| 310 |
| Tensile Strength: Yield (Proof), MPa | 540 to 830 | |
| 220 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 330 | |
| 320 |
| Melting Completion (Liquidus), °C | 1640 | |
| 1660 |
| Melting Onset (Solidus), °C | 1590 | |
| 1610 |
| Specific Heat Capacity, J/kg-K | 550 | |
| 540 |
| Thermal Conductivity, W/m-K | 8.1 | |
| 20 |
| Thermal Expansion, µm/m-K | 9.1 | |
| 8.8 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.4 | |
| 3.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 7.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 37 | |
| 37 |
| Density, g/cm3 | 4.5 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 36 | |
| 31 |
| Embodied Energy, MJ/kg | 580 | |
| 510 |
| Embodied Water, L/kg | 150 | |
| 110 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 89 to 110 | |
| 79 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1380 to 3220 | |
| 230 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 35 | |
| 35 |
| Strength to Weight: Axial, points | 43 to 60 | |
| 19 |
| Strength to Weight: Bending, points | 39 to 48 | |
| 23 |
| Thermal Diffusivity, mm2/s | 3.3 | |
| 8.2 |
| Thermal Shock Resistance, points | 52 to 71 | |
| 24 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 2.5 to 3.5 | |
| 0 |
| Carbon (C), % | 0 to 0.080 | |
| 0 to 0.080 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.2 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 to 0.15 | |
| 0 to 0.18 |
| Titanium (Ti), % | 92.6 to 95.5 | |
| 99.095 to 100 |
| Vanadium (V), % | 2.0 to 3.0 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.4 |