Grade CX2MW Nickel vs. Grade 12 Titanium

Grade CX2MW nickel belongs to the nickel alloys classification, while grade 12 titanium belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is grade CX2MW nickel and the bottom bar is grade 12 titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
110
Elongation at Break, % 34
21
Fatigue Strength, MPa 260
280
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 84
39
Tensile Strength: Ultimate (UTS), MPa 620
530
Tensile Strength: Yield (Proof), MPa 350
410

Thermal Properties

Latent Heat of Fusion, J/g 330
420
Maximum Temperature: Mechanical, °C 980
320
Melting Completion (Liquidus), °C 1550
1660
Melting Onset (Solidus), °C 1490
1610
Specific Heat Capacity, J/kg-K 430
540
Thermal Conductivity, W/m-K 10
21
Thermal Expansion, µm/m-K 12
9.6

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.5
3.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
6.6

Otherwise Unclassified Properties

Base Metal Price, % relative 65
37
Density, g/cm3 8.9
4.5
Embodied Carbon, kg CO2/kg material 12
31
Embodied Energy, MJ/kg 170
500
Embodied Water, L/kg 290
110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
110
Resilience: Unit (Modulus of Resilience), kJ/m3 290
770
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
35
Strength to Weight: Axial, points 19
32
Strength to Weight: Bending, points 18
32
Thermal Diffusivity, mm2/s 2.7
8.5
Thermal Shock Resistance, points 17
37

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.020
0 to 0.080
Chromium (Cr), % 20 to 22.5
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 2.0 to 6.0
0 to 0.3
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 12.5 to 14.5
0.2 to 0.4
Nickel (Ni), % 51.3 to 63
0.6 to 0.9
Nitrogen (N), % 0
0 to 0.030
Oxygen (O), % 0
0 to 0.25
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.8
0
Sulfur (S), % 0 to 0.025
0
Titanium (Ti), % 0
97.6 to 99.2
Tungsten (W), % 2.5 to 3.5
0
Vanadium (V), % 0 to 0.35
0
Residuals, % 0
0 to 0.4