Grade FDC Steel vs. AISI 415 Stainless Steel

Both grade FDC steel and AISI 415 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is grade FDC steel and the bottom bar is AISI 415 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 510
260
Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Reduction in Area, % 42
50
Shear Modulus, GPa 80
76
Tensile Strength: Ultimate (UTS), MPa 1680
900

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 400
780
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 51
24
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
3.1

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
11
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
2.5
Embodied Energy, MJ/kg 19
35
Embodied Water, L/kg 47
110

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 60
32
Strength to Weight: Bending, points 40
26
Thermal Diffusivity, mm2/s 14
6.4
Thermal Shock Resistance, points 50
33

Alloy Composition

Carbon (C), % 0.6 to 0.75
0 to 0.050
Chromium (Cr), % 0 to 0.3
11.5 to 14
Copper (Cu), % 0 to 0.12
0
Iron (Fe), % 98 to 99.4
77.8 to 84
Manganese (Mn), % 0.5 to 1.2
0.5 to 1.0
Molybdenum (Mo), % 0
0.5 to 1.0
Nickel (Ni), % 0
3.5 to 5.5
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.1 to 0.35
0 to 0.6
Sulfur (S), % 0 to 0.025
0 to 0.030