Grade FDC Steel vs. Grade VDSiCrV Steel
Both grade FDC steel and grade VDSiCrV steel are iron alloys. Both are furnished in the hardened (H) condition. They have a very high 99% of their average alloy composition in common.
For each property being compared, the top bar is grade FDC steel and the bottom bar is grade VDSiCrV steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 510 | |
| 630 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 42 | |
| 48 |
| Shear Modulus, GPa | 80 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 1680 | |
| 2100 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 420 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1440 |
| Melting Onset (Solidus), °C | 1410 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 51 | |
| 47 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 | |
| 8.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 2.3 |
| Density, g/cm3 | 7.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.9 |
| Embodied Energy, MJ/kg | 19 | |
| 26 |
| Embodied Water, L/kg | 47 | |
| 50 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 60 | |
| 75 |
| Strength to Weight: Bending, points | 40 | |
| 47 |
| Thermal Diffusivity, mm2/s | 14 | |
| 13 |
| Thermal Shock Resistance, points | 50 | |
| 63 |
Alloy Composition
| Carbon (C), % | 0.6 to 0.75 | |
| 0.5 to 0.7 |
| Chromium (Cr), % | 0 to 0.3 | |
| 0.5 to 1.0 |
| Copper (Cu), % | 0 to 0.12 | |
| 0 to 0.060 |
| Iron (Fe), % | 98 to 99.4 | |
| 96.1 to 97.8 |
| Manganese (Mn), % | 0.5 to 1.2 | |
| 0.4 to 0.9 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.020 |
| Silicon (Si), % | 0.1 to 0.35 | |
| 1.2 to 1.7 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.020 |
| Vanadium (V), % | 0 | |
| 0.1 to 0.25 |