Grade TDSiCr Steel vs. C72150 Copper-nickel
Grade TDSiCr steel belongs to the iron alloys classification, while C72150 copper-nickel belongs to the copper alloys. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is grade TDSiCr steel and the bottom bar is C72150 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 590 | |
| 99 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 150 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 80 | |
| 55 |
| Tensile Strength: Ultimate (UTS), MPa | 1950 | |
| 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 600 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1210 |
| Melting Onset (Solidus), °C | 1400 | |
| 1250 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 410 |
| Thermal Conductivity, W/m-K | 46 | |
| 22 |
| Thermal Expansion, µm/m-K | 13 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 3.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 3.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.2 | |
| 45 |
| Density, g/cm3 | 7.7 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 6.1 |
| Embodied Energy, MJ/kg | 20 | |
| 88 |
| Embodied Water, L/kg | 48 | |
| 270 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 9.1 |
| Stiffness to Weight: Bending, points | 25 | |
| 20 |
| Strength to Weight: Axial, points | 70 | |
| 15 |
| Strength to Weight: Bending, points | 45 | |
| 15 |
| Thermal Diffusivity, mm2/s | 12 | |
| 6.0 |
| Thermal Shock Resistance, points | 58 | |
| 18 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0.5 to 0.6 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0.5 to 0.8 | |
| 0 |
| Copper (Cu), % | 0 to 0.1 | |
| 52.5 to 57 |
| Iron (Fe), % | 96.6 to 97.8 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0.5 to 0.9 | |
| 0 to 0.050 |
| Nickel (Ni), % | 0 | |
| 43 to 46 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 1.2 to 1.6 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.5 |