Hard Drawn ASTM B596 vs. Work Hardened 92-silver 8-tin-oxide
Both hard drawn ASTM B596 and work hardened 92-silver 8-tin-oxide are otherwise unclassified metals. Both are furnished in the cold worked (strain hardened) condition. There are 4 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is hard drawn ASTM B596 and the bottom bar is work hardened 92-silver 8-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 14 | |
| 76 |
| Elongation at Break, % | 4.3 | |
| 34 |
| Shear Strength, MPa | 360 | |
| 210 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 320 |