Heat Treated C95400 Bronze vs. HT C95410 Bronze
Both heat treated C95400 bronze and HT C95410 bronze are copper alloys. Both are furnished in the heat treated (HT) condition. Their average alloy composition is basically identical.
For each property being compared, the top bar is heat treated C95400 bronze and the bottom bar is HT C95410 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 | |
| 200 |
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 8.1 | |
| 9.1 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 43 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 710 | |
| 740 |
| Tensile Strength: Yield (Proof), MPa | 360 | |
| 380 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 230 | |
| 230 |
| Melting Completion (Liquidus), °C | 1040 | |
| 1040 |
| Melting Onset (Solidus), °C | 1030 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 440 |
| Thermal Conductivity, W/m-K | 59 | |
| 59 |
| Thermal Expansion, µm/m-K | 18 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 13 | |
| 13 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 14 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 27 | |
| 28 |
| Density, g/cm3 | 8.2 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 3.3 |
| Embodied Energy, MJ/kg | 53 | |
| 54 |
| Embodied Water, L/kg | 390 | |
| 390 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 48 | |
| 57 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 560 | |
| 630 |
| Stiffness to Weight: Axial, points | 7.7 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 20 | |
| 20 |
| Strength to Weight: Axial, points | 24 | |
| 25 |
| Strength to Weight: Bending, points | 22 | |
| 22 |
| Thermal Diffusivity, mm2/s | 16 | |
| 16 |
| Thermal Shock Resistance, points | 25 | |
| 26 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 10 to 11.5 | |
| 10 to 11.5 |
| Copper (Cu), % | 83 to 87 | |
| 83 to 85.5 |
| Iron (Fe), % | 3.0 to 5.0 | |
| 3.0 to 5.0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 to 1.5 | |
| 1.5 to 2.5 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |