Solder Alloy 111 vs. AWS BAg-2a

Both solder alloy 111 and AWS BAg-2a are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 17 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is solder alloy 111 and the bottom bar is AWS BAg-2a.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 33
83
Poisson's Ratio 0.4
0.32
Shear Modulus, GPa 12
31
Tensile Strength: Ultimate (UTS), MPa 41
170

Thermal Properties

Latent Heat of Fusion, J/g 41
130
Melting Completion (Liquidus), °C 220
710
Melting Onset (Solidus), °C 180
610
Specific Heat Capacity, J/kg-K 180
310
Thermal Expansion, µm/m-K 26
23

Otherwise Unclassified Properties

Density, g/cm3 9.3
8.8
Embodied Carbon, kg CO2/kg material 9.4
30
Embodied Energy, MJ/kg 160
470

Common Calculations

Stiffness to Weight: Axial, points 2.0
5.2
Stiffness to Weight: Bending, points 12
17
Strength to Weight: Axial, points 1.2
5.4
Strength to Weight: Bending, points 2.8
7.8
Thermal Shock Resistance, points 3.5
6.5

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0 to 0.2
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
19 to 21
Copper (Cu), % 0 to 0.080
26 to 28
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0
Lead (Pb), % 48.8 to 50.5
0
Nickel (Ni), % 0 to 0.010
0
Silver (Ag), % 0 to 0.1
29 to 31
Tin (Sn), % 49.5 to 50.5
0
Zinc (Zn), % 0 to 0.0010
21 to 25
Residuals, % 0
0 to 0.15