Solder Alloy 713 vs. AWS BAg-8a

Both solder alloy 713 and AWS BAg-8a are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 15 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is solder alloy 713 and the bottom bar is AWS BAg-8a.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 51
83
Poisson's Ratio 0.36
0.36
Shear Modulus, GPa 19
31
Tensile Strength: Ultimate (UTS), MPa 59
150

Thermal Properties

Latent Heat of Fusion, J/g 62
140
Melting Completion (Liquidus), °C 220
770
Melting Onset (Solidus), °C 220
770
Specific Heat Capacity, J/kg-K 220
290
Thermal Expansion, µm/m-K 22
19

Otherwise Unclassified Properties

Density, g/cm3 7.4
10

Common Calculations

Stiffness to Weight: Axial, points 3.8
4.6
Stiffness to Weight: Bending, points 17
15
Strength to Weight: Axial, points 2.2
4.2
Strength to Weight: Bending, points 4.5
6.3
Thermal Shock Resistance, points 3.7
6.7

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0 to 0.1
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Copper (Cu), % 0.5 to 0.9
26.4 to 28.8
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0
Lead (Pb), % 0 to 0.070
0
Lithium (Li), % 0
0.25 to 0.5
Nickel (Ni), % 0 to 0.010
0
Silver (Ag), % 3.6 to 4.0
71 to 73
Tin (Sn), % 94.6 to 95.9
0
Zinc (Zn), % 0 to 0.0010
0
Residuals, % 0
0 to 0.15