Solder Alloy 713 vs. AWS BNi-8

Solder alloy 713 belongs to the otherwise unclassified metals classification, while AWS BNi-8 belongs to the nickel alloys. There are 17 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is solder alloy 713 and the bottom bar is AWS BNi-8.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 51
180
Poisson's Ratio 0.36
0.32
Shear Modulus, GPa 19
67
Tensile Strength: Ultimate (UTS), MPa 59
570

Thermal Properties

Latent Heat of Fusion, J/g 62
390
Melting Completion (Liquidus), °C 220
1010
Melting Onset (Solidus), °C 220
980
Specific Heat Capacity, J/kg-K 220
480
Thermal Expansion, µm/m-K 22
13

Otherwise Unclassified Properties

Density, g/cm3 7.4
7.9
Embodied Carbon, kg CO2/kg material 18
8.2
Embodied Energy, MJ/kg 300
120

Common Calculations

Stiffness to Weight: Axial, points 3.8
12
Stiffness to Weight: Bending, points 17
24
Strength to Weight: Axial, points 2.2
20
Strength to Weight: Bending, points 4.5
19
Thermal Shock Resistance, points 3.7
17

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.0010
0 to 0.050
Antimony (Sb), % 0 to 0.1
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Carbon (C), % 0
0 to 0.060
Cobalt (Co), % 0
0 to 0.1
Copper (Cu), % 0.5 to 0.9
4.0 to 5.0
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0
Lead (Pb), % 0 to 0.070
0
Manganese (Mn), % 0
21.5 to 24.5
Nickel (Ni), % 0 to 0.010
61.6 to 68.5
Phosphorus (P), % 0
0 to 0.020
Selenium (Se), % 0
0 to 0.0050
Silicon (Si), % 0
6.0 to 8.0
Silver (Ag), % 3.6 to 4.0
0
Sulfur (S), % 0
0 to 0.020
Tin (Sn), % 94.6 to 95.9
0
Titanium (Ti), % 0
0 to 0.050
Zinc (Zn), % 0 to 0.0010
0
Zirconium (Zr), % 0
0 to 0.050
Residuals, % 0
0 to 0.5