Solder Alloy 713 vs. Grade 363 Molybdenum

Both solder alloy 713 and grade 363 molybdenum are otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is solder alloy 713 and the bottom bar is grade 363 molybdenum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 51
310
Elongation at Break, % 16
6.2 to 11
Poisson's Ratio 0.36
0.31
Shear Modulus, GPa 19
120
Tensile Strength: Ultimate (UTS), MPa 59
580 to 720

Thermal Properties

Latent Heat of Fusion, J/g 62
370
Specific Heat Capacity, J/kg-K 220
250
Thermal Expansion, µm/m-K 22
7.0

Otherwise Unclassified Properties

Density, g/cm3 7.4
10
Embodied Carbon, kg CO2/kg material 18
28
Embodied Energy, MJ/kg 300
330

Common Calculations

Stiffness to Weight: Axial, points 3.8
17
Stiffness to Weight: Bending, points 17
22
Strength to Weight: Axial, points 2.2
16 to 20
Strength to Weight: Bending, points 4.5
15 to 17
Thermal Shock Resistance, points 3.7
19 to 24

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0 to 0.1
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Carbon (C), % 0
0.010 to 0.030
Copper (Cu), % 0.5 to 0.9
0
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0 to 0.010
Lead (Pb), % 0 to 0.070
0
Molybdenum (Mo), % 0
99.3 to 99.5
Nickel (Ni), % 0 to 0.010
0 to 0.0020
Nitrogen (N), % 0
0 to 0.0020
Oxygen (O), % 0
0 to 0.0030
Silicon (Si), % 0
0 to 0.010
Silver (Ag), % 3.6 to 4.0
0
Tin (Sn), % 94.6 to 95.9
0
Titanium (Ti), % 0
0.4 to 0.55
Zinc (Zn), % 0 to 0.0010
0
Zirconium (Zr), % 0
0.060 to 0.12