MakeItFrom.com
Menu (ESC)

ISO-WD32250 Magnesium vs. S32506 Stainless Steel

ISO-WD32250 magnesium belongs to the magnesium alloys classification, while S32506 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ISO-WD32250 magnesium and the bottom bar is S32506 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
200
Elongation at Break, % 4.5 to 8.6
21
Fatigue Strength, MPa 170 to 210
330
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 17
81
Shear Strength, MPa 180 to 190
440
Tensile Strength: Ultimate (UTS), MPa 310 to 330
710
Tensile Strength: Yield (Proof), MPa 240 to 290
500

Thermal Properties

Latent Heat of Fusion, J/g 340
300
Maximum Temperature: Mechanical, °C 120
1100
Melting Completion (Liquidus), °C 600
1450
Melting Onset (Solidus), °C 550
1400
Specific Heat Capacity, J/kg-K 980
480
Thermal Conductivity, W/m-K 130
16
Thermal Expansion, µm/m-K 26
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 25
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 130
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 13
20
Density, g/cm3 1.8
7.8
Embodied Carbon, kg CO2/kg material 24
3.9
Embodied Energy, MJ/kg 160
54
Embodied Water, L/kg 950
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 14 to 26
130
Resilience: Unit (Modulus of Resilience), kJ/m3 630 to 930
620
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 67
25
Strength to Weight: Axial, points 49 to 51
25
Strength to Weight: Bending, points 58 to 60
23
Thermal Diffusivity, mm2/s 72
4.3
Thermal Shock Resistance, points 19 to 20
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
24 to 26
Iron (Fe), % 0
60.8 to 67.4
Magnesium (Mg), % 94.9 to 97.1
0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
3.0 to 3.5
Nickel (Ni), % 0
5.5 to 7.2
Nitrogen (N), % 0
0.080 to 0.2
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 0.9
Sulfur (S), % 0
0 to 0.015
Tungsten (W), % 0
0.050 to 0.3
Zinc (Zn), % 2.5 to 4.0
0
Zirconium (Zr), % 0.45 to 0.8
0
Residuals, % 0 to 0.3
0