Monel 400 vs. EN 2.4654 Nickel
Both Monel 400 and EN 2.4654 nickel are nickel alloys. They have 58% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is Monel 400 and the bottom bar is EN 2.4654 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 160 | |
| 200 |
| Elongation at Break, % | 20 to 40 | |
| 17 |
| Fatigue Strength, MPa | 230 to 290 | |
| 460 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Shear Modulus, GPa | 62 | |
| 77 |
| Shear Strength, MPa | 370 to 490 | |
| 770 |
| Tensile Strength: Ultimate (UTS), MPa | 540 to 780 | |
| 1250 |
| Tensile Strength: Yield (Proof), MPa | 210 to 590 | |
| 850 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 1000 | |
| 1000 |
| Melting Completion (Liquidus), °C | 1350 | |
| 1390 |
| Melting Onset (Solidus), °C | 1300 | |
| 1330 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 460 |
| Thermal Conductivity, W/m-K | 23 | |
| 13 |
| Thermal Expansion, µm/m-K | 14 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 50 | |
| 75 |
| Density, g/cm3 | 8.9 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 7.9 | |
| 10 |
| Embodied Energy, MJ/kg | 110 | |
| 150 |
| Embodied Water, L/kg | 250 | |
| 340 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 180 | |
| 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 1080 | |
| 1810 |
| Stiffness to Weight: Axial, points | 10 | |
| 13 |
| Stiffness to Weight: Bending, points | 21 | |
| 23 |
| Strength to Weight: Axial, points | 17 to 25 | |
| 42 |
| Strength to Weight: Bending, points | 17 to 21 | |
| 31 |
| Thermal Diffusivity, mm2/s | 6.1 | |
| 3.3 |
| Thermal Shock Resistance, points | 17 to 25 | |
| 37 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 1.2 to 1.6 |
| Boron (B), % | 0 | |
| 0.0030 to 0.010 |
| Carbon (C), % | 0 to 0.3 | |
| 0.020 to 0.1 |
| Chromium (Cr), % | 0 | |
| 18 to 21 |
| Cobalt (Co), % | 0 | |
| 12 to 15 |
| Copper (Cu), % | 28 to 34 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 2.5 | |
| 0 to 2.0 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 3.5 to 5.0 |
| Nickel (Ni), % | 63 to 72 | |
| 50.6 to 62.5 |
| Phosphorus (P), % | 0 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.15 |
| Sulfur (S), % | 0 to 0.024 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 2.8 to 3.3 |
| Zirconium (Zr), % | 0 | |
| 0.020 to 0.080 |