Nickel 617 vs. EN 1.0070 Steel

Nickel 617 belongs to the nickel alloys classification, while EN 1.0070 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is nickel 617 and the bottom bar is EN 1.0070 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 40
9.1
Fatigue Strength, MPa 220
210
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 510
440
Tensile Strength: Ultimate (UTS), MPa 740
740
Tensile Strength: Yield (Proof), MPa 280
350

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Maximum Temperature: Mechanical, °C 1010
400
Melting Completion (Liquidus), °C 1380
1470
Melting Onset (Solidus), °C 1330
1430
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
53
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
6.8
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
7.8

Otherwise Unclassified Properties

Base Metal Price, % relative 75
1.7
Density, g/cm3 8.5
7.9
Embodied Carbon, kg CO2/kg material 10
1.4
Embodied Energy, MJ/kg 140
18
Embodied Water, L/kg 350
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
56
Resilience: Unit (Modulus of Resilience), kJ/m3 190
320
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 24
26
Strength to Weight: Bending, points 21
23
Thermal Diffusivity, mm2/s 3.5
14
Thermal Shock Resistance, points 21
23

Alloy Composition

Aluminum (Al), % 0.8 to 1.5
0
Boron (B), % 0 to 0.0060
0
Carbon (C), % 0.050 to 0.15
0
Chromium (Cr), % 20 to 24
0
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 0 to 3.0
99.876 to 100
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 8.0 to 10
0
Nickel (Ni), % 44.5 to 62
0
Nitrogen (N), % 0
0 to 0.014
Phosphorus (P), % 0
0 to 0.055
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.015
0 to 0.055