Nickel 625 vs. S46500 Stainless Steel
Nickel 625 belongs to the nickel alloys classification, while S46500 stainless steel belongs to the iron alloys. They have a modest 27% of their average alloy composition in common, which, by itself, doesn't mean much. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is nickel 625 and the bottom bar is S46500 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 33 to 34 | |
| 2.3 to 14 |
| Fatigue Strength, MPa | 240 to 320 | |
| 550 to 890 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 79 | |
| 75 |
| Shear Strength, MPa | 530 to 600 | |
| 730 to 1120 |
| Tensile Strength: Ultimate (UTS), MPa | 790 to 910 | |
| 1260 to 1930 |
| Tensile Strength: Yield (Proof), MPa | 320 to 450 | |
| 1120 to 1810 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 980 | |
| 780 |
| Melting Completion (Liquidus), °C | 1350 | |
| 1450 |
| Melting Onset (Solidus), °C | 1290 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 470 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 80 | |
| 15 |
| Density, g/cm3 | 8.6 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 14 | |
| 3.6 |
| Embodied Energy, MJ/kg | 190 | |
| 51 |
| Embodied Water, L/kg | 290 | |
| 120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 220 to 250 | |
| 43 to 210 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 26 to 29 | |
| 44 to 68 |
| Strength to Weight: Bending, points | 22 to 24 | |
| 33 to 44 |
| Thermal Shock Resistance, points | 22 to 25 | |
| 44 to 67 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.4 | |
| 0 |
| Carbon (C), % | 0 to 0.1 | |
| 0 to 0.020 |
| Chromium (Cr), % | 20 to 23 | |
| 11 to 12.5 |
| Cobalt (Co), % | 0 to 1.0 | |
| 0 |
| Iron (Fe), % | 0 to 5.0 | |
| 72.6 to 76.1 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 0.25 |
| Molybdenum (Mo), % | 8.0 to 10 | |
| 0.75 to 1.3 |
| Nickel (Ni), % | 58 to 68.9 | |
| 10.7 to 11.3 |
| Niobium (Nb), % | 3.2 to 4.2 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.25 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 to 0.4 | |
| 1.5 to 1.8 |