Quarter-hard 80-silver 20-cadmium-oxide vs. Quarter-hard ASTM B628
Both quarter-hard 80-silver 20-cadmium-oxide and quarter-hard ASTM B628 are otherwise unclassified metals. Both are furnished in the quarter-hard temper. There are 8 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is quarter-hard 80-silver 20-cadmium-oxide and the bottom bar is quarter-hard ASTM B628.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 9.9 | |
| 10 |
| Electrical Conductivity: Equal Volume, % IACS | 70 | |
| 84 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 64 | |
| 75 |
| Elongation at Break, % | 1.1 | |
| 5.6 |
| Shear Strength, MPa | 220 | |
| 250 |
| Strength to Weight: Axial, points | 11 | |
| 12 |
| Strength to Weight: Bending, points | 12 | |
| 13 |
| Tensile Strength: Ultimate (UTS), MPa | 390 | |
| 430 |