Z13004 Zinc vs. AWS BVAg-18

Z13004 zinc belongs to the zinc alloys classification, while AWS BVAg-18 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is Z13004 zinc and the bottom bar is AWS BVAg-18.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
82
Poisson's Ratio 0.25
0.36
Shear Modulus, GPa 35
30
Tensile Strength: Ultimate (UTS), MPa 93
180

Thermal Properties

Latent Heat of Fusion, J/g 110
140
Melting Completion (Liquidus), °C 410
720
Melting Onset (Solidus), °C 390
600
Specific Heat Capacity, J/kg-K 390
280
Thermal Expansion, µm/m-K 26
19

Otherwise Unclassified Properties

Density, g/cm3 6.6
9.7
Embodied Carbon, kg CO2/kg material 2.8
59
Embodied Energy, MJ/kg 53
930

Common Calculations

Stiffness to Weight: Axial, points 7.4
4.7
Stiffness to Weight: Bending, points 23
15
Strength to Weight: Axial, points 3.9
5.1
Strength to Weight: Bending, points 7.0
7.3
Thermal Shock Resistance, points 2.9
8.1

Alloy Composition

Aluminum (Al), % 0 to 0.0020
0
Cadmium (Cd), % 0 to 0.0030
0 to 0.0010
Carbon (C), % 0
0 to 0.0050
Copper (Cu), % 0 to 0.0030
28.5 to 31.5
Iron (Fe), % 0 to 0.0030
0
Lead (Pb), % 0 to 0.0030
0 to 0.0020
Phosphorus (P), % 0
0 to 0.0020
Silver (Ag), % 0
59 to 61
Tin (Sn), % 0 to 0.0010
9.5 to 10.5
Zinc (Zn), % 99.985 to 100
0 to 0.0010