Z13004 Zinc vs. EN 1.1191 Steel

Z13004 zinc belongs to the zinc alloys classification, while EN 1.1191 steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is Z13004 zinc and the bottom bar is EN 1.1191 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
190
Elongation at Break, % 30
16 to 17
Poisson's Ratio 0.25
0.29
Shear Modulus, GPa 35
72
Tensile Strength: Ultimate (UTS), MPa 93
630 to 700
Tensile Strength: Yield (Proof), MPa 76
310 to 440

Thermal Properties

Latent Heat of Fusion, J/g 110
250
Maximum Temperature: Mechanical, °C 90
400
Melting Completion (Liquidus), °C 410
1460
Melting Onset (Solidus), °C 390
1420
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 110
48
Thermal Expansion, µm/m-K 26
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 37
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 11
2.1
Density, g/cm3 6.6
7.8
Embodied Carbon, kg CO2/kg material 2.8
1.4
Embodied Energy, MJ/kg 53
19
Embodied Water, L/kg 340
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 26
83 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 33
260 to 510
Stiffness to Weight: Axial, points 7.4
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 3.9
22 to 25
Strength to Weight: Bending, points 7.0
21 to 22
Thermal Diffusivity, mm2/s 44
13
Thermal Shock Resistance, points 2.9
20 to 22

Alloy Composition

Aluminum (Al), % 0 to 0.0020
0
Cadmium (Cd), % 0 to 0.0030
0
Carbon (C), % 0
0.42 to 0.5
Chromium (Cr), % 0
0 to 0.4
Copper (Cu), % 0 to 0.0030
0
Iron (Fe), % 0 to 0.0030
97.3 to 99.08
Lead (Pb), % 0 to 0.0030
0
Manganese (Mn), % 0
0.5 to 0.8
Molybdenum (Mo), % 0
0 to 0.1
Nickel (Ni), % 0
0 to 0.4
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0
0 to 0.4
Sulfur (S), % 0
0 to 0.035
Tin (Sn), % 0 to 0.0010
0
Zinc (Zn), % 99.985 to 100
0