SAE-AISI 1021 Steel vs. ACI-ASTM CE30 Steel

Both SAE-AISI 1021 steel and ACI-ASTM CE30 steel are iron alloys. They have 61% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1021 steel and the bottom bar is ACI-ASTM CE30 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130 to 150
180
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 17 to 27
11
Fatigue Strength, MPa 190 to 300
170
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
79
Tensile Strength: Ultimate (UTS), MPa 480 to 530
630
Tensile Strength: Yield (Proof), MPa 260 to 450
310

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1410
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 52
14
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
19
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.4
3.4
Embodied Energy, MJ/kg 18
49
Embodied Water, L/kg 46
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 84 to 110
59
Resilience: Unit (Modulus of Resilience), kJ/m3 180 to 530
240
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17 to 19
23
Strength to Weight: Bending, points 17 to 18
21
Thermal Diffusivity, mm2/s 14
3.6
Thermal Shock Resistance, points 15 to 17
13

Alloy Composition

Carbon (C), % 0.18 to 0.23
0 to 0.3
Chromium (Cr), % 0
26 to 30
Iron (Fe), % 98.8 to 99.22
55.1 to 66
Manganese (Mn), % 0.6 to 0.9
0 to 1.5
Nickel (Ni), % 0
8.0 to 11
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0
0 to 2.0
Sulfur (S), % 0 to 0.050
0 to 0.040