SAE-AISI 1021 Steel vs. ASTM A387 Grade 91 Class 2

Both SAE-AISI 1021 steel and ASTM A387 grade 91 class 2 are iron alloys. They have 89% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1021 steel and the bottom bar is ASTM A387 grade 91 class 2.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130 to 150
200
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 17 to 27
20
Fatigue Strength, MPa 190 to 300
330
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
75
Shear Strength, MPa 310 to 320
420
Tensile Strength: Ultimate (UTS), MPa 480 to 530
670
Tensile Strength: Yield (Proof), MPa 260 to 450
470

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 400
600
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
26
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
8.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
10

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
7.0
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
2.6
Embodied Energy, MJ/kg 18
37
Embodied Water, L/kg 46
88

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 84 to 110
120
Resilience: Unit (Modulus of Resilience), kJ/m3 180 to 530
580
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17 to 19
24
Strength to Weight: Bending, points 17 to 18
22
Thermal Diffusivity, mm2/s 14
6.9
Thermal Shock Resistance, points 15 to 17
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.020
Carbon (C), % 0.18 to 0.23
0.080 to 0.12
Chromium (Cr), % 0
8.0 to 9.5
Iron (Fe), % 98.8 to 99.22
87.3 to 90.3
Manganese (Mn), % 0.6 to 0.9
0.3 to 0.6
Molybdenum (Mo), % 0
0.85 to 1.1
Nickel (Ni), % 0
0 to 0.4
Niobium (Nb), % 0
0.060 to 0.1
Nitrogen (N), % 0
0.030 to 0.070
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0
0.2 to 0.5
Sulfur (S), % 0 to 0.050
0 to 0.010
Titanium (Ti), % 0
0 to 0.010
Vanadium (V), % 0
0.18 to 0.25
Zirconium (Zr), % 0
0 to 0.010