SAE-AISI 1021 Steel vs. EN 1.4412 Stainless Steel

Both SAE-AISI 1021 steel and EN 1.4412 stainless steel are iron alloys. They have 66% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1021 steel and the bottom bar is EN 1.4412 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130 to 150
140
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 17 to 27
34
Fatigue Strength, MPa 190 to 300
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
79
Tensile Strength: Ultimate (UTS), MPa 480 to 530
490
Tensile Strength: Yield (Proof), MPa 260 to 450
230

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1000
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
15
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
20
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.4
4.1
Embodied Energy, MJ/kg 18
56
Embodied Water, L/kg 46
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 84 to 110
140
Resilience: Unit (Modulus of Resilience), kJ/m3 180 to 530
140
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17 to 19
17
Strength to Weight: Bending, points 17 to 18
18
Thermal Diffusivity, mm2/s 14
3.9
Thermal Shock Resistance, points 15 to 17
11

Alloy Composition

Carbon (C), % 0.18 to 0.23
0 to 0.070
Chromium (Cr), % 0
18 to 20
Iron (Fe), % 98.8 to 99.22
60.4 to 69
Manganese (Mn), % 0.6 to 0.9
0 to 1.5
Molybdenum (Mo), % 0
3.0 to 3.5
Nickel (Ni), % 0
10 to 13
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0
0 to 1.5
Sulfur (S), % 0 to 0.050
0 to 0.030