SAE-AISI 1023 Steel vs. N08031 Stainless Steel

Both SAE-AISI 1023 steel and N08031 stainless steel are iron alloys. They have a modest 33% of their average alloy composition in common, which, by itself, doesn't mean much. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1023 steel and the bottom bar is N08031 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 17 to 29
45
Fatigue Strength, MPa 180 to 270
290
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
81
Shear Strength, MPa 280 to 300
510
Tensile Strength: Ultimate (UTS), MPa 430 to 480
730
Tensile Strength: Yield (Proof), MPa 240 to 410
310

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 53
12
Thermal Expansion, µm/m-K 12
18

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
39
Density, g/cm3 7.9
8.1
Embodied Carbon, kg CO2/kg material 1.4
7.1
Embodied Energy, MJ/kg 18
96
Embodied Water, L/kg 45
240

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 77 to 100
270
Resilience: Unit (Modulus of Resilience), kJ/m3 150 to 450
230
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 15 to 17
25
Strength to Weight: Bending, points 16 to 17
22
Thermal Diffusivity, mm2/s 14
3.1
Thermal Shock Resistance, points 14 to 15
14

Alloy Composition

Carbon (C), % 0.2 to 0.25
0 to 0.015
Chromium (Cr), % 0
26 to 28
Copper (Cu), % 0
1.0 to 1.4
Iron (Fe), % 99.06 to 99.5
29 to 36.9
Manganese (Mn), % 0.3 to 0.6
0 to 2.0
Molybdenum (Mo), % 0
6.0 to 7.0
Nickel (Ni), % 0
30 to 32
Nitrogen (N), % 0
0.15 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0
0 to 0.3
Sulfur (S), % 0 to 0.050
0 to 0.010