SAE-AISI 1065 Steel vs. EN 1.6570 Steel

Both SAE-AISI 1065 steel and EN 1.6570 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1065 steel and the bottom bar is EN 1.6570 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 230
270 to 340
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 14
11 to 17
Fatigue Strength, MPa 270 to 340
500 to 660
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Tensile Strength: Ultimate (UTS), MPa 710 to 780
910 to 1130
Tensile Strength: Yield (Proof), MPa 430 to 550
760 to 1060

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
440
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
40
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 12
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
3.9
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.7
Embodied Energy, MJ/kg 19
23
Embodied Water, L/kg 46
56

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 74 to 90
120 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 490 to 820
1520 to 3010
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 28
32 to 40
Strength to Weight: Bending, points 23 to 24
27 to 31
Thermal Diffusivity, mm2/s 14
11
Thermal Shock Resistance, points 25 to 27
27 to 33

Alloy Composition

Carbon (C), % 0.6 to 0.7
0.28 to 0.35
Chromium (Cr), % 0
1.0 to 1.4
Iron (Fe), % 98.3 to 98.8
94 to 96.2
Manganese (Mn), % 0.6 to 0.9
0.6 to 1.0
Molybdenum (Mo), % 0
0.3 to 0.5
Nickel (Ni), % 0
1.6 to 2.1
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0
0 to 0.6
Sulfur (S), % 0 to 0.050
0 to 0.015