SAE-AISI 1137 Steel vs. Grade VDSiCrV Steel

Both SAE-AISI 1137 steel and grade VDSiCrV steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1137 steel and the bottom bar is grade VDSiCrV steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 210
630
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Reduction in Area, % 34 to 39
48
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 700 to 760
2100

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 400
420
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 51
47
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 12
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
2.3
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.4
1.9
Embodied Energy, MJ/kg 19
26
Embodied Water, L/kg 48
50

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25 to 27
75
Strength to Weight: Bending, points 22 to 24
47
Thermal Diffusivity, mm2/s 14
13
Thermal Shock Resistance, points 21 to 23
63

Alloy Composition

Carbon (C), % 0.32 to 0.39
0.5 to 0.7
Chromium (Cr), % 0
0.5 to 1.0
Copper (Cu), % 0
0 to 0.060
Iron (Fe), % 97.8 to 98.3
96.1 to 97.8
Manganese (Mn), % 1.4 to 1.7
0.4 to 0.9
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0
1.2 to 1.7
Sulfur (S), % 0.080 to 0.13
0 to 0.020
Vanadium (V), % 0
0.1 to 0.25