SAE-AISI 1137 Steel vs. SAE-AISI 1006 Steel

Both SAE-AISI 1137 steel and SAE-AISI 1006 steel are iron alloys. They have a very high 98% of their average alloy composition in common.

For each property being compared, the top bar is SAE-AISI 1137 steel and the bottom bar is SAE-AISI 1006 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 210
94 to 100
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 17
22 to 33
Fatigue Strength, MPa 250 to 400
140 to 210
Poisson's Ratio 0.29
0.29
Reduction in Area, % 34 to 39
49 to 62
Shear Modulus, GPa 73
73
Shear Strength, MPa 430 to 460
230
Tensile Strength: Ultimate (UTS), MPa 700 to 760
340 to 370
Tensile Strength: Yield (Proof), MPa 370 to 650
180 to 300

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
53
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 12
7.9

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
18
Embodied Water, L/kg 48
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 81 to 100
75 to 95
Resilience: Unit (Modulus of Resilience), kJ/m3 360 to 1130
86 to 240
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 27
12 to 13
Strength to Weight: Bending, points 22 to 24
14 to 15
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 21 to 23
10 to 11

Alloy Composition

Carbon (C), % 0.32 to 0.39
0 to 0.080
Iron (Fe), % 97.8 to 98.3
99.43 to 99.75
Manganese (Mn), % 1.4 to 1.7
0.25 to 0.4
Phosphorus (P), % 0 to 0.040
0 to 0.040
Sulfur (S), % 0.080 to 0.13
0 to 0.050

Comparable Variants