SAE-AISI 1144 Steel vs. ASTM A356 Grade 10

Both SAE-AISI 1144 steel and ASTM A356 grade 10 are iron alloys. They have a very high 96% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1144 steel and the bottom bar is ASTM A356 grade 10.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220 to 230
200
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 17
23
Fatigue Strength, MPa 280 to 430
300
Poisson's Ratio 0.29
0.29
Reduction in Area, % 34 to 40
39
Shear Modulus, GPa 72
74
Tensile Strength: Ultimate (UTS), MPa 750 to 840
670
Tensile Strength: Yield (Proof), MPa 420 to 690
430

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Maximum Temperature: Mechanical, °C 400
460
Melting Completion (Liquidus), °C 1450
1470
Melting Onset (Solidus), °C 1410
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
39
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
3.9
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.8
Embodied Energy, MJ/kg 19
23
Embodied Water, L/kg 47
59

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 91 to 110
130
Resilience: Unit (Modulus of Resilience), kJ/m3 480 to 1290
480
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 27 to 30
24
Strength to Weight: Bending, points 23 to 25
22
Thermal Diffusivity, mm2/s 14
11
Thermal Shock Resistance, points 22 to 24
19

Alloy Composition

Carbon (C), % 0.4 to 0.48
0 to 0.2
Chromium (Cr), % 0
2.0 to 2.8
Iron (Fe), % 97.5 to 98
94.4 to 96.6
Manganese (Mn), % 1.4 to 1.7
0.5 to 0.8
Molybdenum (Mo), % 0
0.9 to 1.2
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0
0 to 0.6
Sulfur (S), % 0.24 to 0.33
0 to 0.030