SAE-AISI 1541 Steel vs. EN 1.0540 Steel

Both SAE-AISI 1541 steel and EN 1.0540 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1541 steel and the bottom bar is EN 1.0540 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 220
190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 17
14
Fatigue Strength, MPa 260 to 420
210
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
72
Shear Strength, MPa 440 to 480
400
Tensile Strength: Ultimate (UTS), MPa 720 to 790
660
Tensile Strength: Yield (Proof), MPa 390 to 680
330

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
48
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
19
Embodied Water, L/kg 48
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78 to 100
75
Resilience: Unit (Modulus of Resilience), kJ/m3 410 to 1250
290
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 28
23
Strength to Weight: Bending, points 23 to 24
22
Thermal Diffusivity, mm2/s 14
13
Thermal Shock Resistance, points 23 to 25
21

Alloy Composition

Carbon (C), % 0.36 to 0.44
0.47 to 0.55
Chromium (Cr), % 0
0 to 0.4
Iron (Fe), % 97.8 to 98.3
97.2 to 98.9
Manganese (Mn), % 1.4 to 1.7
0.6 to 0.9
Molybdenum (Mo), % 0
0 to 0.1
Nickel (Ni), % 0
0 to 0.4
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0
0 to 0.4
Sulfur (S), % 0 to 0.050
0 to 0.045